Ion-beam sputtering, fabrication of oxide-semiconductor-on-silicon (OSOS) solar cells, results in cells of 12% efficiency. Ion-beam sputtering technique is compatible with low-cost continuous fabrication and requires no high-temperature processing.
Heterojunction diodes of indium tin oxide films sputtered on to p-silicon using ion-beam techniques display significant photovoltaic effects when exposed to sunlight. Galvanomagnetic and optical measurements confirm that the oxide films are highly degenerate transparent semiconductors. At a tin oxide concentration of 10%, an open-circuit voltage of 0.51 V was observed along with a short-circuit current of 32 mA/sq cm, a fill factor of 0.70, and a conversion efficiency of 12%. As the concentration was raised to 70%, the voltage remained steady, the current fell to 27 mA/sq cm, and the fill factor fell to 0.60
Oxide semiconductor on silicon (OSOS) solar cells have been fabricated from various indium tin oxide (In2O3)x(SnO2)1-x compositions sputtered onto p-type single crystal silicon substrates with a neutralized argon ion beam. High temperature processing or annealing was not required. The highest efficiency was achieved with x = 0.91 and was 12 percent. The cells are environmentally rugged, chemically stable, and show promise for still higher efficiencies. Moreover, the ion beam sputtering fabrication technique is amenable to low cost, continuous processing.