Characterization of nickel-copper alloy specimens processed as a part of the M553 sphere forming experiment during the Skylab 1 and 2 flight
Both processed nickel-copper alloy specimens apparently completely melted by the electron beam in the Skylab M512 materials processing facility and either floated free in space, but collided with some smooth flat surface before solidifying, or remained attached to its support post during solidification. Both specimens had a smooth flat area on the surface due to this adherence during solidification. The nominal composition of the alloy before processing in space was 70 percent Ni and 30 percent Cu. Tests show that a considerable amount of copper was lost during processing by evaporation. It was further found that less copper was present in the cap areas, particularly at the surface, than was in the remainder of the specimens. The microchemistry of the dendrites and interdendritic regions, however, is in agreement with the phase diagram for this alloy. The measured densities of these specimens were less than the theoretical density of the alloy due to the amount of porosity present, however, no large voids were found by radiographic techniques.