Influence of Thermophysical Property Variability on Thermal Predictions of Ti-6Al-4V
The additive manufacturing (AM) industry has experienced rapid growth in recent decades as industrial interest in the process has grown. Because of this, there are many groups interested in simulations of the AM process. However, the influence of thermophysical property variability on the melt pool geometry during processing of various AM alloys is unclear. The goal of my work at NASA Langley Research Center (LaRC) was to characterize this influence on Ti-6Al-4V during AM processing alongside developing a tool to enable equivalent studies on other AM materials. To facilitate this process, a database tool was developed to contain and organize thermophysical data previously reported by primary sources. The specific thermophysical properties of interest for this study were density, specific heat capacity, and conductivity. Thermal diffusivity was calculated using the other three properties. This data was then fit with a Gaussian distribution and then randomly sampled from using Monte Carlo random value sampling. Using the Rosenthal equation, this sample data was used to simulate the temperature field during additive manufacturing and extract the melt pool geometry. Specifically, the melt pool’s length, width, and depth. This process was repeated an arbitrary number of times, with the default being 1000. Once this information was obtained, histograms were made showing the distributions of the sizes of the melt pool’s length, width, and depth. Representative statistical metrics of the distributions were calculated (mean, standard deviation, and coefficient of variance). This work found that at the simulated processing values, the melt pool’s width and depth had a 5.7% variation while the length had a 3.2% variation. Additionally, a tool was constructed to graph a thermal color map representation of the melt pool for specific, arbitrary values of density, specific heat, and conductivity. This tool allowed for more efficient plotting of individual queries of the thermophysical properties. The results that were observed in the research were that values reported in literature vary and this variance can have a significant impact on the simulation. Predictions of the melt pool’s dimensions show that length has a standard deviation of approximately 6 μm, width has a standard deviation of approximately 5 μm, and depth can vary by approximately 3 μm. Considering the mean sizes of length, width, and depth are 185 μm, 88 μm, and 44 μm respectively, such a deviation is significant. This shows that depth, for example, could be more than 10% larger or smaller than expected. This demonstrates that variability in the reported thermophysical properties are not negligible and should be expected to have an influence on the results of the laser powder bed fusion additive manufacturing process. When simulating this process in the future, measures should be taken to account for this discrepancy and the uncertainty involved