Ignition characteristics of the nickel-based alloy UNS N07001 in pressurized oxygen

The development of ignition and combustion in pressurized oxygen atmospheres was studied for the nickel-based alloy UNS N07001. Ignition of the alloy was achieved by heating the top surface of a cylindrical specimen with a continuous-wave CO2 laser. Two heating procedures were used. In the first, laser power was adjusted to maintain an approximately linear increase in surface temperature. In the second, laser power was periodically increased until autoheating (self-heating) was established. It was found that the alloy would autoheat to combustion from temperatures below the solidus temperature. In addition, the alloy had a tendency to develop combustion zones (hot spots) at high oxygen pressures when the incremental (step) heating test mode was used. Unique points on the temperature-time curves that describe certain events are defined and the temperatures at which these events occur are given for the oxygen pressure range of 1.72 to 13.8 MPa (250 to 2000 psia).

Bransford, J. W.↗
NASA NTRS1986

Ignition and combustion temperatures determined by laser heating

A laser heating technique and facility have been developed to study metal ignition and combustion in high-pressure oxygen. The ignition and combustion temperatures, estimates of oxidation rates, and ignition and combustion morphology can be determined. This facility and the laser heating techniques are described. Examples of the type of data obtained are presented and discussed. The ignition temperature curves for an aluminum alloy - Unified Numbering System (UNS) A96061, a stainless steel - UNS S30200, and two nickel alloys - UNS N07718 and N04400 are given.

Bransford, J. W.↗
NASA NTRS1985

Ignition of metals in high pressure oxygen

A description of an experimental facility used to determine the ignition and combustion characteristics of metallic materials is given. The results obtained for aluminum 6061, 302 stainless steel, and the nickel alloy - N06625 are presented.

Bransford, J. W.↗
NASA NTRS1985

Beam Window for Pressure Chambers

Window resists products of combustion experiments. Sodium chloride window seals over chamber pressures from 0.1 to 13.8 MPa while absorbing minimal energy from CO2 laser beam that passes through it into chamber. Window inexpensive and easily replacable.

Bransford, J. W.↗
NASA NTRS1984

Ignition phenomena of bulk aluminum alloy as a function of oxygen pressure

An ignition phenomena of 6061 aluminum alloy was investigated as a function of oxygen pressure. Cylindrical aluminum alloy specimens were ignited in a pure oxygen environment by a focused CW CO2 laser beam. The experiments were conducted at oxygen pressures ranging from 0.084 to 2.413 MPa. The temperature history of the entire upper surface of the specimen and of a 0.5 mm diameter spot located initially at the center of the specimen top surface was recorded by using a commercial two-color ratio pyrometer and a fast-response, narrow-band, two-color pyrometer. Mass, brightness, and interior temperatures (for certain experiments) were also recorded throughout the experiment. The results show that the surface temperatures at ignition of the alloy obtained from the temperature curves are below the melting temperature of the aluminum oxide and are slightly dependent on oxygen pressure. The data indicate that the ignition mechanism is complex and probably composed of several phenomena acting both separately and in conjunction with each other.

Nguyen, K.↗
NASA NTRS1981

Laser-initiated combustion studies of selected aluminum, copper, iron, and nickel alloys

The results of combustion studies at atmospheric pressure on ten metal alloys are presented. The alloys studied were aluminum alloys 1100, 2219, 6061, and tensile-50; 304, 347 and 21-6-9 stainless steel; inconel 600; beryllium copper and a bronze. It was found that once ignition was achieved all alloys would generally burn to completion. The overall combustion process appears to obey a first order rate process. Preliminary conclusions are presented along with recommendations for future work.

Bransford, J. W.↗
NASA NTRS1980

LOX/GOX mechanical impact tester assessment

The performances of three existing high pressure oxygen mechanical impact test systems were tested at two different test sites. The systems from one test site were fabricated from the same design drawing, whereas the system tested at the other site was of different design. Energy delivered to the test sample for each test system was evaluated and compared. Results were compared to the reaction rates obtained.

Bransford, J. W.↗
NASA NTRS1975

Flammability study of materials in oxygen environments

Report presents flame-propagation rates and flammability ratings of 780 specimens of commercially available plastics, elastomers, coatings, fabrics, and other sheet materials. Test results are also given for over 1970 samples of most commonly used electrical harnesses, connectors, and potting compounds.