High strength aluminum stamping
The invention provides a method of manufacturing a component formed of an aluminum alloy for use in an automotive vehicle application, for example those requiring high strength, light-weight, and a complex three-dimensional shape. The method begins by providing a blank formed of an aluminum alloy which is already solution heat treated and tempered, and thus has a temper designation of about T4. The method further includes heating the blank to a temperature of 150° C. to 350° C., preferably 190° C. to 225° C. The method next includes quickly transferring the blank to a hot or warm forming apparatus, and stamping the blank to form the complex three-dimensional shape. Immediately after the forming step, the component has a temper designation of about T6, but preferably not greater than T6, and thus is ready for use in the automotive vehicle application without any post heat treatment or machining.