Engineering Papers⌕ Search

Engineering topics

Bhattacharyya, Madhumanti

Publications and source records attributed to Bhattacharyya, Madhumanti.

7 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Chloride-Induced Stress Corrosion Cracking of Friction Stir-Welded 304L Stainless Steel: Effect of Microstructure and Temperature

Dry storage canisters of used nuclear fuels are fabricated using SUS 304L stainless steel. Chloride-induced stress corrosion cracking (CISCC) is one of the major failure modes of dry storage canisters. The cracked canisters can be repaired by friction stir welding (FSW), a low-heat input ‘solid-phase’ welding process. It is important to evaluate the ClSCC resistance of the friction stir welded material. Stress corrosion cracking (SCC) studies were carried out on mill-annealed base materials and friction stir welded 304L stainless U-bend specimens in 3.5% NaCl + 5 N H2SO4 solution at room temperature and boiling MgCl2 solution at 155 °C. The engineering stress on the outer fiber of the FSW U-bend specimen was ~60% higher than that of the base metal (BM). In spite of the higher stress level of the FSW, both materials (FSW and BM) showed almost similar SCC failure times in the two different test solutions. The SCC occurred in the thermo-mechanically affected zone (TMAZ) of the FSW specimens in the 3.5% NaCl + 5 N H2SO4 solution at room temperature, while the stirred zone (SZ) was relatively crack-free. The failure occurred at the stirred zone when tested in the boiling MgCl2 solution. Hydrogen reduction was the cathodic reaction in the boiling MgCl2 solution, which promoted hydrogen-assisted cracking of the heavily deformed stirred zone. The emergence of the slip step followed by passive film rupture and dissolution of the slip step could be the SCC events in the 3.5% NaCl + 5 N H2SO4 solution at room temperature. However, the slip step height was not sufficient to cause passivity breakdown in the fine-grained SZ. Therefore, the SCC occurred in the partially recrystallized softer TMAZ. Overall, the friction-stirred 304L showed higher tolerance to ClSCC than the 304L base metal.

304L austenitic stainless steel↗
DOE OSTI2022

Room temperature corrosion behaviour of plastically deformed AISI 304 stainless steel by friction stir welding in neutral and acidified chloride solutions

Severe plastic deformation of 304L stainless steel plate was carried out by friction stirring under an isothermal tool temperature at 825°C. The friction stirred zone showed extensive grain refinement, high fraction of low angle grain boundaries due to dislocation rearrangement, Σ3 and Σ9 special grain boundaries and discrete Fe–Cr–Mn-rich particles. Electrochemical polarisation measurements were done on the base metal (BM) and friction stir welded (FSW) specimens in the neutral and acidified 3.5% NaCl solutions. The BM showed marginally better pitting resistance in the neutral chloride solution than the FSW because of a larger fraction of special grain boundaries, and larger grain size. Whereas in acidified 3.5% NaCl solution, the FSW showed better corrosion resistance than the BM. Furthermore, the surface film of the FSW had a lower impedance and a lower defect concentration than the BM indicating higher diffusivity of point defects in the FSW.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Indentation investigation of 304L stainless steel friction stir weld simulated crack repair

Simulated cracks were repaired in 304L stainless steel using low temperature friction stir welding. Indentation studies were carried out to understand the effect of microstructural features on the mechanical property variation across the weld and to measure the size of the weld zones with a quantitative technique. Microhardness and nanoindentation hardness profiles were constructed on a transverse section across the weld. The data obtained were correlated by extrapolating the nanoindentation hardness to greater depths which showed that the nanoindentation hardness closely reflects the microhardness values throughout the weld. Finally, grain size in the stir zone (SZ) was found to vary with the tool temperature which, in turn, alters the nanoindentation modulus variability and higher tool temperature resulted in widening of the SZ.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Evaluation of residual stresses in isothermal friction stir welded 304L stainless steel plates

Friction stir welding was performed on 304L SS plates in order to heal simulated cracks created by electrical discharge machining. Two different tool temperatures (825 and 725 °C) were chosen for this study. Both neutron diffraction and X-ray diffraction techniques were employed to evaluate the residual stresses along two orthogonal reference directions, longitudinal (syy) and transverse (sxx). The former technique was also used to measure residual stresses at various depths. It was found that, at 1 mm depth from the top surface inside the stir zone (SZ), the longitudinal component was tensile in nature while the transverse component was compressive. The nature and magnitude of the residual stress fields, and the position of the peak residual stresses were found to vary with the weld depth. The SZ of the 725 °C weld exhibited higher peak stress than 825 °C weld mainly due to a lack of stress relief at the lower temperature.

Friction stir welding, Steel↗
DOE OSTI2020

Pitting behavior of friction stir repair-welded 304L stainless steel in 3.5% NaCl solution at room temperature: role of grain and defect structures

Stainless steel (SS) canisters used for storing spent nuclear waste are prone to chloride-induced stress corrosion cracking. Friction stir welding (FSW), being a low heat input process, can be used for repair welding of these canisters. In this study, an artificial crack was introduced on the 304L SS coupons by an electric discharge machining process. The artificial crack was repair-welded by FSW by maintaining the tool temperature a constant at two levels (725 and 825 °C). Friction stirring significantly reduced the grain size of the stirred zone (SZ) from about 47 to 2–4 μm. The fraction of low-angle grain boundaries increased in the SZ from 2 to 37–43%. Here, on the other hand, the fraction of special grain boundaries (Σ3 and Σ9) that was ~ 50% in the base metal reduced to < 10% in the SZ. During friction stirring, the oxide layer of artificial crack was broken and aligned to form a spiral defect called lazy-S structure. All these microstructural changes affected the corrosion behavior of the FSW specimens when tested in 3.5% NaCl at room temperature using cyclic polarization, chronoamperometry, and electrochemical impedance spectroscopy. The FSW specimens showed lower polarization resistance and lower transpassive potential than those of the base metal specimens. However, the pitting protection potentials of the FSW specimens were higher than that of the base metal. The pitting behavior of the FSW specimens was influenced more by the preferential attack on the lazy-S region than by passive film breakdown. The flat band potentials of the passive film formed on the FSW specimens were more positive than that of base metal. The charge carrier density of passive film formed on the FSW specimens was higher than that of the base metal. The higher fraction of low-angle grain boundaries present in the FSW specimens could supply more number of misorientation dislocations at the metal/film interface which could form anion vacancies by a climb process leading to formation of oxide at these locations without stressing the substrate. Therefore, low-angle boundaries are considered helpful for formation of stress-free passive films that will be highly stable and enhance both pitting and stress corrosion cracking resistance.

Dry storage canister↗
DOE OSTI2020

A FEASIBILITY STUDY ON CRACK REPAIR IN AUSTENITIC STAINLESS STEEL DRY STORAGE CANISTERS USING ISOTHERMAL FRICTION STIR WELDING

In recent time, solid state crack repair techniques in spent nuclear fuel dry storage canisters (SNF-DSC) have garnered significant interest. Plates of austenitic stainless steels are usually arc welded to fabricate the cylindrical canisters which are prone to chloride-induced stress corrosion cracking. Friction stir welding (FSW) is considered to be a potential candidate for damage repair. In this work, electrical discharge machining was used to simulate cracks in 304L stainless steel plates of 12.7 mm thickness. Subsequently, isothermal FSW was carried out at two different temperatures (725 and 825°C) in order to repair the simulated crack. Microstructure-mechanical property correlations in FSWed plates were studied in detail. Significant grain refinement observed in the stir zone (SZ) was attributed to dynamic recrystallization occurring during FSW. A comparison of Vickers microhardness showed higher hardness and homogeneity in the 725°C SZ than its 825°C counterpart. The fraction of S3 boundary is found to be low in the SZ as compared to base metal (BM). Yield strength of the joints was found to be approximately 100 MPa higher than that of the BM accompanied by a drop in ductility by a factor of 2. Residual stress profile across 825°C weld was measured using x-ray diffraction.

Bhattacharyya, Madhumanti↗