NASA NTRS1993

Polyimides Made From 4,4'-Isophthaloyldiphthalic Anhydride

High-performance, thermoplastic, amorphous, and semicrystalline materials obtained. In experiments, twelve high-temperature, high-performance polyimide compositions based on 4,4'-isophthaloyldiphthalic anhydride (IDPA) prepared and characterized. Tough, film-forming, polyimides insoluble in organic solvents obtained in most cases. Three materials semicrystalline. Materials offer potential for development of semicrystalline polyimides having enhanced resistances to solvents and caustic chemicals, higher tensile strengths and moduli, enhanced thermo-oxidative stabilities below their melting temperatures, and enhanced melt processability, especially when heated to melting temperatures. Several exhibited excellent long-term thermo-oxidative stability when subjected to isothermal thermogravimetric analysis (ITGA) at temperatures of 300 degrees C and 350 degrees C in air. One area of application, manufacturing of lighter and stronger aircraft and spacecraft structures.

Pratt, J. Richard↗

NASA NTRS1990

Process for crosslinking methylene-containing aromatic polymers with ionizing radiation

A process for crosslinking aromatic polymers containing radiation-sensitive methylene groups (-CH2-) by exposing the polymers to ionizing radiation thereby causing crosslinking of the polymers through the methylene groups is described. Crosslinked polymers are resistant to most organic solvents such as acetone, alcohols, hydrocarbons, methylene, chloride, chloroform, and other halogenated hydrocarbons, to common fuels and to hydraulic fluids in contrast to readily soluble uncrosslinked polymers. In addition, the degree of crosslinking of the polymers depends upon the percentage of the connecting groups which are methylene which ranges from 5 to 50 pct and preferably from 25 to 50 pct of the connecting groups, and is also controlled by the level of irradiation which ranges from 25 to 1000 Mrads and preferably from 25 to 250 Mrads. The temperature of the reaction conditions ranges from 25 to 200 C and preferably at or slightly above the glass transition temperature of the polymer. The crosslinked polymers are generally more resistant to degradation at elevated temperatures such as greater than 150 C, have a reduced tendency to creep under load, and show no significant embrittlement of parts fabricated from the polymers.

Bell, Vernon L.↗

NASA NTRS1988

Graft copolymers from poly(2,6-dimethylphenylene oxide) and pivalolactone

The copolyether-polyester system resulting from the anionic graft polymerization of pivalolactone onto poly(2,6-dimethylphenylene oxide) has been formulated with differing graft densities and graft segment lengths. Wide angle X-ray scattering studies on these materials indicated an increased crystalline order with increased PVL segments/graft for similarly annealed specimens and a decrease in such order with increasing carboxylation.

Bell, Vernon L.↗

NASA NTRS1987

Polyether-polyester graft copolymer

Described is a polyether graft polymer having improved solvent resistance and crystalline thermally reversible crosslinks. The copolymer is prepared by a novel process of anionic copolymerization. These polymers exhibit good solvent resistance and are well suited for aircraft parts. Previous aromatic polyethers, also known as polyphenylene oxides, have certain deficiencies which detract from their usefulness. These commercial polymers are often soluble in common solvents including the halocarbon and aromatic hydrocarbon types of paint thinners and removers. This limitation prevents the use of these polyethers in structural articles requiring frequent painting. In addition, the most popular commercially available polyether is a very high melting plastic. This makes it considerably more difficult to fabricate finished parts from this material. These problems are solved by providing an aromatic polyether graft copolymer with improved solvent resistance and crystalline thermally reversible crosslinks. The graft copolymer is formed by converting the carboxyl groups of a carboxylated polyphenylene oxide polymer to ionic carbonyl groups in a suitable solvent, reacting pivalolactone with the dissolved polymer, and adding acid to the solution to produce the graft copolymer.

Bell, Vernon L.↗

NASA NTRS1987

Cross-Linking Aromatic Polymers With Ionizing Radiation

Resistance to heat and solvents increased. Certain aromatic polymers containing radiation-sensitive methylene groups cross-linked through methylene groups upon exposure to ionizing radiation. Cross-linked polymers resistant to most organic solvents and generally more resistant to high temperatures, with less tendency to creep under load. No significant embrittlement of parts fabricated from these polymers when degree of cross-linking, as controlled by irradiation dose, kept at moderate level.

Bell, Vernon L.↗

NASA NTRS1987

Processing Conjugated-Diene-Containing Polymers

Diels-Alder reaction used to cross-linked thermoplastics. Process uses Diels-Alder reaction to cross-link and/or extend conjugated-diene-containing polymers by reacting them with bis-unsaturated dienophiles results in improved polymer properties. Quantities of diene groups required for cross-linking varies from very low to very high concentrations. Process also used to extend, or build up molecular weights of, low-molecular-weight linear polymers with terminal conjugated dienic groups.

Bell, Vernon L.↗

NASA NTRS1986

Isomeric bismaleimides and polyaspartimides

The properties of a series of bismaleimides and polyaspartimides synthesized from the 3,3', 3,4', and 4,4' isomers of diaminodiphenylmethane are described and compared. The effects of the amine isomerism on the characteristics of bismaleimides and their polymers are investigated. It is observed that the 3,3'-bismaleimide had the highest crystalline melting point, the 4,4' isomer the lowest, and the 3,4'-bismaleimide was slightly above the all-para compounds; for the polyaspartimides, the all-para combinations had the highest glass transition temperature (218 C) and the all-meta the lowest (168 C). The data reveal that strong, flexible films were obtained only from the polyaspartimides made from the 4,4'-diamine/4,4'bismaleimide and the 3,4'-diamine/3,4'bismaleimide combinations; and the tensile properties of the 3,4'polymer films were as good as those of the 4,4 'polymer.

Bell, Vernon L.↗

NASA NTRS1977

Process for crosslinking and extending conjugated diene-containing polymers

A process using a Diels-Alder reaction which increases the molecular weight and/or crosslinks polymers by reacting the polymers with bisunsaturated dienophiles is developed. The polymer comprises at least 75% by weight based on the reaction product, has a molecular weight of at least 5000 and a plurality of conjugated 1,3-diene systems incorporated into the molecular structure. A dienophile reaction with the conjugated 1,3-diene of the polymer is at least 1% by weight based on the reaction product. Examples of the polymer include polyesters, polyamides, polyethers, polysulfones and copolymers. The bisunsaturated dienophiles may include bis-maleimides, bis maleic and bis tumaric esters and amides. This method for expanding the molecular weight chains of the polymers, preferable thermoplastics, is advantageous for processing or fabricating thermoplastics. A low molecular weight thermoplastic is converted to a high molecular weight plastic having improved strength and toughness for use in the completed end use article.

Bell, Vernon L.↗