Microstructural evolution in doped high entropy alloys NiCoFeCr-3X (X=Pd/Al/Cu) under irradiation

Commonly studied equatomic single-phase FCC high entropy alloys based on 3d transition metals like NiCoFeCr do not provide adequate strength and radiation resistance at high doses for nuclear structural applications. In the current study, the major alloying effects like lattice distortion, ordering and clustering tendencies were investigated by adding low concentration of Pd, Al, or Cu respectively to study the doping effects on the ion irradiation response of NiCoFeCr alloy. The alloys were irradiated with 3 MeV Ni 2+ ions at 500 °C to a fluence of 1 × 10 17 /cm 2 at a beam flux of approximately 2.8 × 10 12 ions/cm 2 /s. The microstructural evolution upon irradiation i.e., formation of dislocation networks, radiation induced segregation and precipitation, and void formation were studied in detail. Further, post-irradiation characterization results showed that a Pd addition leads to a high void nucleation rate but controlled void growth, which may be attributed to increased lattice distortion. In Al added HEA, our microstructural analysis indicates that radiation induced ordered L1 2 precipitates do not affect void swelling significantly. Cu addition led to Cu precipitation that drastically suppressed dislocation density and void swelling of the alloy. Additionally, a model was developed to qualitatively describe the trend in void swelling of typical FCC alloys under ion irradiation. This model was able to qualitatively explain the suppression and reappearance of void swelling in ion irradiated alloys that generally occurs near the region with peak implanted ion concentration.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Nanoprecipitates to Enhance Radiation Tolerance in High-Entropy Alloys

The growth of advanced energy technologies for power generation is enabled by the design, development, and integration of structural materials that can withstand extreme environments, such as high temperatures, radiation damage, and corrosion. High-entropy alloys (HEAs) are a class of structural materials in which suitable chemical elements in four or more numbers are mixed to typically produce single-phase concentrated solid solution alloys (CSAs). Many of these alloys exhibit good radiation tolerance like limited void swelling and hardening up to relatively medium radiation doses (tens of displacements per atom (dpa)); however, at higher radiation damage levels (>50 dpa), some HEAs suffer from considerable void swelling limiting their near-term acceptance for advanced nuclear reactor concepts. In this study, we developed a HEA containing a high density of Cu-rich nanoprecipitates distributed in the HEA matrix. The Cu-added HEA, NiCoFeCrCu 0.12 , shows excellent void swelling resistance and negligible radiation-induced hardening upon irradiation up to high radiation doses (i.e., higher than 100 dpa). The void swelling resistance of the alloy is measured to be significantly better than NiCoFeCr CSA and austenitic stainless steels. Density functional theory simulations predict lower vacancy and interstitial formation energies at the coherent interfaces between Cu-rich nanoprecipitates and the HEA matrix. The alloy maintained a high sink strength achieved via nanoprecipitates and the coherent interface with the matrix at a high radiation dose (~50 dpa). From our experiments and simulations, the effective recombination of radiation-produced vacancies and interstitials at the coherent interfaces of the nanoprecipitates is suggested to be the critical mechanism responsible for the radiation tolerance of the alloy. Furthermore, the materials design strategy based on incorporating a high density of interfaces can be applied to high-entropy alloy systems to improve their radiation tolerance.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Understanding effects of chemical complexity on helium bubble formation in Ni-based concentrated solid solution alloys based on elemental segregation measurements

Here, helium bubble formation and swelling were systematically studied in Ni-based concentrated solid solution alloys containing different numbers and types of elements. Our microscopy analysis showed that although increasing the alloy chemical complexity helps suppress bubble formation in general, there is no monotonic relationship between the bubble growth rate and the number of alloying elements. Certain elements (e.g., Fe and Pd) are more effective in suppressing bubble growth than others (e.g., Cr and Mn). Atom probe tomography was applied to accurately measure elemental segregation around bubbles, revealing unique effects of certain alloying elements on vacancy migration towards bubbles. More specifically, the high vacancy mobility via Cr sites leads to a large vacancy flux and an increased bubble size, while the high degree of atomic size mismatch introduced by Pd helps deflect vacancy flow away from bubbles and decrease the amount of swelling. The effects identified in this study provide new strategies to design concentrated solid solutions with superior resistance to swelling.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Deformation mechanisms in single crystal Ni-based concentrated solid solution alloys by nanoindentation

Nanoindentation is a critical technique to probe mechanical properties at the micrometer and sub-micrometer scales, accompanied by challenges from indentation size effect, pile-up/sink-in effect, and strain rate sensitivity. In this work, different nanoindentation techniques have been employed to explore Ni-based concentrated solid solution alloys (CSAs) with the addition of 3d transition metal elements including Co, Cr, Mn, and Fe, including unique single-crystal Ni, NiCo, NiFe, Ni 80 Cr 20 , and NiCoFeCr samples with (100) surfaces. A procedure of nanoindentation tests and data analysis/correction have been developed, and a data set of hardness, elastic modulus, strain rate sensitivity, and activation volume for Ni-based CSAs are provided, including the less explored binary alloys such as Ni 80 Cr 20 and Ni 80 Mn 20 . The results show that the type of alloying elements is more critical than the number of elements in strengthening: Co does not provide strengthening in NiCo, while Cr, Mn, and Fe are effective strengthening elements. Cr is the most effective among all the 3d transition metal elements. Furthermore, atomic-level lattice distortion is responsible for the strengthening and the role of stacking fault energy is insignificant in Ni-based CSAs at room temperature. In summary, nanoindentation shows increasing promise as a reliable and fast tool to provide comprehensive mechanical information for new alloy design and development.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Role of chemical disorder on radiation-induced defect production and damage evolution in NiFeCoCr

Understanding chemical disorder in many concentrated solid solution alloys (CSAs) at the levels of electrons and atoms has attracted increasing attention as a path forward to reveal and identify underlying mechanisms for extraordinary mechanical properties and improved radiation tolerance. Single-phase NiFeCoCr CSA is a common base for many high-entropy alloys (HEAs) that have shown improved mechanical strength and radiation tolerance. In this study, defect production and damage evolution in NiFeCoCr under ion irradiation at room temperature to dose over 20 dpa are determined using ion channeling technique along both <100> and <110> directions utilizing multiple probing beam energies. The results obtained from the multi-axial and multi-energy channeling analysis are compared with those previously obtained for Ni crystals irradiated under similar conditions. The influence of chemical complexity on defect production and clustering at early-stage under room temperature irradiation up to dose of 1 dpa is discussed based on positron annihilation spectroscopy results. Defect structure evaluation in Ni and NiFeCoCr is also discussed based on transmission electron microscopy results over a prolonged irradiation at both room and elevated temperatures. Compared with chemically complex NiFeCoCr, larger dislocation loops thus less lattice strain are expected to form in pure Ni. Moreover, the role of chemical disorder in this CSA is also investigated based on ab initio calculations using large supercells. Finally, to understand the impact of chemical complexity effect on defect structure evolution, this integrated research effort attempts to link the relatively large charge redistribution due to difference in valence electron counts resulting from alloying different 3d transition metal elements, moderate lattice distortion arising from similar adaptable atomic size, and notable suppressed or delayed damage evolution in NiFeCoCr.

36 MATERIALS SCIENCE↗
DOE OSTI2021

The dynamic evolution of swelling in nickel concentrated solid solution alloys through in situ property monitoring

Defects and microstructural features spanning the atomic level to the microscale play deterministic roles in the expressed properties of materials. Yet studies of material evolution in response to environmental stimuli most often correlate resulting performance with one dominant microstructural feature only. In this work, the dynamic evolution of swelling in a series of Ni-based concentrated solid solution alloys under high-temperature irradiation exposure is observed using continuous, in situ measurements of thermoelastic properties in bulk specimens. Unlike traditional evaluation techniques which account only for volumetric porosity identified using electron microscopy, direct property evaluation provides an integrated response across all defect length scales. In particular, the evolution in elastic properties during swelling is found to depend significantly on the entire size spectrum of defects, from the nano- to meso-scales, some of which are not resolvable in imaging. Observed changes in thermal transport properties depend sensitively on the partitioning of electronic and lattice thermal conductivity. This emerging class of in situ experiments, which directly measure integrated performance in relevant conditions, provides unique insight into material dynamics otherwise unavailable using traditional methods.

36 MATERIALS SCIENCE↗
DOE OSTI2021

First-principles calculation of lattice distortions in four single phase high entropy alloys with experimental validation

Exceptional properties of high entropy alloys (HEAs) are attributed to the disordered random solid solution of multiple alloying elements. Despite numerous studies, the fundamental understanding at the electronic and atomic levels is still missing. We report a comparative study of four fcc HEAs of NiFeCoCr and NiFeCoCrX (X = Mn, Cu, or Pd) based on ab initio calculations using large supercells with 500 atoms in equal composition. After fully optimizing their structures using the VASP package, their electronic structure, interatomic bonding, partial charge distribution, and mechanical properties are calculated and compared, revealing the intricate interdependence among them. A novel parameter based on the quantum mechanical metric for internal cohesion, the total bond order density (TBOD), is used to interpret the calculated properties. The highest TBOD is found in Cantor alloy NiFeCoCrMn but lower in NiFeCoCrPd. The atomic radii vary depending on their local chemical environment. The resulting lattice distortions is validated experimentally in NiFeCoCrMn and NiFeCoCrPd. Moreover, modeling of Cu and Pd clustering in the supercell shows they have lower total energy in agreement with the observation of Cu-enhanced nano-participates in NiFeCoCrCu and Pd-induced concentration wave in NiFeCoCrPd HEAs.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Diffusion-mediated chemical concentration variation and void evolution in ion-irradiated NiCoFeCr high-entropy alloy

High-entropy alloys (HEAs) are proposed as potential structural materials for advanced nuclear systems, but little is known about the response of matrix chemistry in HEAs upon irradiation. Here, we reveal a substantial change of matrix chemical concentration as a function of irradiation damage (depth) in equiatomic NiCoFeCr HEA irradiated by 3 MeV Ni ions. After ion irradiation, the matrix contains more Fe/Cr in depth shallower than ~900–1000 nm but more Ni/Co from ~900–1000 nm to the end of the ion-damaged region due to the preferential diffusion of vacancies through Fe/Cr. Preferential diffusion also facilitates migration of vacancies from high radiation damage region to low radiation damage region, leading to no void formation below ~900–1000 nm and void formation around the end of the ion-damaged region at a fluence of 5 × 10 16 cm -2 (~123 dpa, displacements per atom, peak dose under full cascade mode). As voids grow significantly at an increased fluence (8 × 10 16 cm -2 , 196 dpa), the matrix concentration does not change dramatically due to new voids formed below ~900–1000 nm.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2021

Diffusion-mediated chemical concentration variation and void evolution in ion-irradiated NiCoFeCr high-entropy alloy

High-entropy alloys (HEAs) are proposed as potential structural materials for advanced nuclear systems, but little is known about the response of matrix chemistry in HEAs upon irradiation. Here, we reveal a substantial change of matrix chemical concentration as a function of irradiation damage (depth) in equiatomic NiCoFeCr HEA irradiated by 3 MeV Ni ions. After ion irradiation, the matrix contains more Fe/Cr in depth shallower than ~900–1000 nm but more Ni/Co from ~900–1000 nm to the end of the ion-damaged region due to the preferential diffusion of vacancies through Fe/Cr. Preferential diffusion also facilitates migration of vacancies from high radiation damage region to low radiation damage region, leading to no void formation below ~900–1000 nm and void formation around the end of the ion-damaged region at a fluence of 5 × 10 16 cm –2 (~123 dpa, displacements per atom, peak dose under full cascade mode). As voids grow significantly at an increased fluence (8 × 10 16 cm –2 , 196 dpa), the matrix concentration does not change dramatically due to new voids formed below ~900–1000 nm.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Origin of increased helium density inside bubbles in Ni (1–$x$) Fe $x$ alloys

Due to virtually no solubility, He atoms implanted or created inside materials tend to form bubbles, which are known to damage material properties through embrittlement. Higher He density in nano-sized bub- bles was observed both experimentally and computationally in Ni (1–$x$) Fe $x$ -alloy samples compared to Ni. The bubbles in the Ni (1–$x$) Fe $x$ -alloys were observed to be faceted, whereas in elemental Ni they were more spherical. Molecular dynamics simulations showed that stacking fault structures formed around bubbles at maximum He density. Higher Fe concentrations stabilize stacking fault structures, suppress evolution of dislocation network around bubbles and suppress complete dislocation emission, leading to higher He density.

36 MATERIALS SCIENCE↗
DOE OSTI2020

STEM Characterization of Dislocation Loops in Irradiated FCC Alloys

In this study, we demonstrate the methodology systematically developed for dislocation loop (perfect and faulted loops) imaging and analysis in irradiated face-centered-cubic (FCC) alloys using scanning transmission electron microscopy (STEM). On-zone [001] STEM imaging was identified as the preferred choice for its accuracy and effectiveness based on the comparison with other dislocation loop imaging techniques including: (i) on-zone STEM imaging using other major low-index zone axes, (ii) kinematic two-beam conditions bright field imaging near the [001] zone axis in conventional TEM (CTEM) mode, and (iii) Rel-Rod CTEM dark-field (DF) imaging near the [011] zone axis. The effect of STEM collection angle on the contrast formation of dislocation loops was also investigated. The developed method was confirmed by imaging all populations of perfect and faulted loops of types a/2$\langle$110$\rangle${110} and a/3$\langle$111$\rangle${111} found in an ion irradiated Ni40Fe40Cr20 alloy. The proposed STEM-based technique can easily identify said loops with a size greater than 10 nm without any assumptions such as those commonly made using the conventional Rel-Rod CTEM-DF technique. The recommended methodology in this study is developed as a quick and convenient tool that can be generally applied to irradiated FCC-based materials due to their common crystallography.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2020

An exploratory study on helium mobility in amorphous and crystallized bulk metallic glasses

In this study, Zr 52.5 Cu 17.9 Ni 14.6 Al 10 Ti 5 and Cu 60 Zr 20 Hf 10 Ti 10 amorphous and crystallized bulk metallic glasses (BMGs) were implanted at room temperature by 150 keV 3 He + ions to fluences of 2 × 10 15 cm -2 and 5 × 10 15 cm -2 , producing peak implanted He concentrations of ~1,100 and 3,500 appm, respectively. Nuclear reaction analysis (NRA) performed on post-implantation annealed samples at various temperatures between 250 and 600 °C (~0.30 to 0.75 of the absolute melting temperature T m of the BMGs) revealed no appreciable He migration. Complementary thermal desorption spectroscopy (TDS) on as-implanted samples, which involved in situ annealing, showed appreciable He release only at temperatures higher than ~700 °C (~0.76-0.90 T m ) in all the samples. Half or more of the implanted He did not desorb up to the maximum investigated TDS annealing temperature of 770 °C (~0.85-0.97 T m ). The lack of pronounced He diffusion up to 600 °C as observed from the NRA and TDS data was attributed to He trapping in free volume sites present in the BMGs, which seems to play a similar role to vacancies in crystalline materials. It was also observed that in both the amorphous and crystallized forms of the Zr BMG, the sample implanted to the lower fluence released more He as compared to the sample implanted with a higher fluence. The crystalline forms of both the Cu and Zr BMGs released more He as compared to their amorphous counterparts.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Dislocation loop evolution and radiation hardening in nickel-based concentrated solid solution alloys

Effects of chemical composition, ion irradiation dose and temperature on unfaulting of irradiation induced Frank dislocation loops to perfect loops in two nickel based single-phase solid solution alloys, Ni–20Fe and NiFe–20Cr, have been studied. The fraction of Frank loops decreases with irradiation dose from 7.2 to 38.4 dpa at 500°C, but with more Frank loops remaining in the ternary alloy. However, perfect loops and dislocation networks become the dominant features of defects at 580°C in both alloys. The results indicate a thermally assisted loop unfaulting process that may be hindered by more sluggish defect motion in the alloy with more chemical components. Nano-indentation with both continuous stiffness method and single indentation method are used to measure radiation hardening. Loop unfaulting in both alloys irradiated at 580°C reduced radiation hardening while significant hardening is observed after irradiation at 500°C. The quasi-static single indentation method exhibits lower hardness results compared to continuous stiffness method, because dislocations induced from the cyclic loading in the latter method get relaxed and stabilized, resulting in higher resistance to the indenter.

36 MATERIALS SCIENCE↗