Inconel 718, nickel-based alloy used extensively for high-temperature structural service, welded repeatedly without detriment to its strength. According to NASA report, tests show 12 repairs on same weld joint do not adversely affect ultimate tensile strenth, yield strength, fatigue strength, metallurgical grain structures, or ability of weld joint to respond to post weld heat treatments.
Four-phase study was launched to determine welding conditions conductive to crater cracks and to establish procedures for fixing them. Results of study are published in brief report.
Excessive weld peaking can be corrected in heavy aluminum structures according to procedure. When peaking varies along weld joint, weld energy must be varied to compensate for nonuniformity.
The welding of the nickel base, heat resistant alloys that are used extensively for welded Shuttle engine components revealed solidification cracking characteristics at weld termination points. If not detected and removed, these crater cracks may cause costly component failure. To better understand this characteristic, welding termination techniques were studied and methods developed to eliminate crater cracks. It was determined that weld termination solidification cracking can be eliminated by controlled decrease of welding current, welding voltage, wire feed, and travel speed.
Weld peaking is usually undesirable in any welded structure. In heavy structures, the forces involved in the welding process become very large and difficult to handle. With the shuttle's solid rocket booster, the weld peaking resulted in two major problems: (1) reduced mechanical properties across the weld joint, and (2) fit-up difficulties in subsequent assembly operation. Peaking from the weld shrinkage forces can be fairly well predicted in simple structures; however, in welding complicated assemblies, the amount of peaking is unpredictable because of unknown stresses from machining and forming, stresses induced by the fixturing, and stresses from welds in other parts of the assembly. When excessive peaking is encountered, it can be corrected using the shrinkage forces resulting from the welding process. Application of these forces is discussed in this report.
The Space Shuttle Solid Rocket Booster (SRB) forward and aft skirts were designed with fracture control considerations used in the design data. Fracture control is based on reliance upon nondestructive evaluation (NDE) techniques to detect potentially critical flaws. In the aerospace industry, welds on aluminum in the thicknesses (0.500 to 1.375 in.) such as those encountered on the SRB skirts are normally welded from both sides to minimize distortion. This presents a problem with the potential presence of undefined areas of incomplete fusion and the inability to detect these potential flaws by NDE techniques. To eliminate the possibility of an undetectable defect, weld joint design was revised to eliminate blind root penetrations. Weld parameters and mechanical property data were developed to verify the adequacy of the new joint design.