Exploring the elastic and electronic properties of chromium molybdenum diboride alloys
We perform first-principles calculations to study the structural, mechanical, thermal, electronic, and magnetic properties of Cr 1-x Mo x B 2 for x = 0.25, 0.33, 0.50, 0.67 and 0.75. Based on structural search methods, we determine the ground-state structure for each concentration. The ternaries are either monoclinic (x = 0.25, 0.75) or trigonal (x = 0.33, 0.50, 0.67). The calculated mechanical properties reveal that the strength of Cr 1-x Mo x B 2 is maximized for x = 0.50. Cr 0.5 Mo 0.5 B 2 exhibits excellent mechanical properties (B = 298 GPa, Y = 558 GPa, G = 235 Gpa, ν = 0.19, H v =27 GPa), surpassing those of β-MoB 2 at a lower cost. All of these ternaries are hard alloys with Vickers hardness greater than 24 GPa. Chemical bonding analysis demonstrates that the strength of the new compounds is related to the alternating planar and buckled B-B layers, as well as the strong TM-B bonds. Finally, the enhanced strength of Cr 0.5 Mo 0.5 B 2 is a consequence of the high density of strong interlayer Cr-Mo metallic bonds around the Fermi level.