DOE OSTI2022

Results of Initial Alloy 617 High Temperature Crack Growth Testing

Crack propagation data can provide valuable insights when performing a safety evaluation for a component. Alloy 617 is qualified in Section III, Division 5 of the American Society of Mechanical Engineers (ASME) Boiler and Pressure Vessel Code (BPVC) for elevated-temperature nuclear service up to 950°C. Little is known, however, about subcritical crack-growth phenomena in Alloy 617. Previous crack-growth studies of Alloy 617 did not investigate temperatures across the range which is currently qualified in Section III, Division 5. High-temperature crack-growth testing in air and in reactor-grade helium can provide data for establishing the crack-growth correlations in support of an ASME BPVC Section XI high-temperature flaw evaluation Code Case. Idaho National Laboratory (INL) has previously performed crack-growth testing, but the equipment requires revitalization. This report provides the status of crack-growth testing in Alloy 617 at INL.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2022

Graphite Degradation Modeling and Analysis

A graphite component in a nuclear reactor core is subjected to variety of stresses and can experience degradation during normal and off-normal operation. Understanding how a graphite component will behave in service is essential to ensuring core structural stability and safe reactor operation. This report summarizes a graphite modeling tool currently under development at Idaho National Laboratory. The model incorporates several of the anticipated stresses during service and includes the effects of oxidation and irradiation prior to turnaround. This tool is intended to be used to help assess the design of graphite components by utilizing design code rules found in Section III, Division 5 of the American Society of Mechanical Engineering Boiler and Pressure Vessel Code. Specifically, the tool uses the methodologies found within the Full and Simplified assessments from Article HHA-3000 to verify that a graphite component has an acceptably low probability of failure.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Graphite Oxidation Modeling

Oxidation modeling importance ASME consideration Effect on graphite properties Model Overview Numerical Model Oxidation Diffusion Reaction Kinetics Model Parameterization Example problems Editing the model Simple problem example Conclusions Coupling to stress analysis Oxidation result analysis

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

ASME BPVC Section III Division 5 Application

Using AMSE assessments Simplified assessment overview Implementation Limitation and important considerations Example problems Full Assessment overview Implementation Limitation and important considerations Example problems Limitation of the code

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

GCR: Alloy 617 Crack Growth Testing Status

Environment can have an appreciable effect on crack growth. This presentation provides updates on environmental crack growth testing of Alloy 617 at INL.

36 MATERIALS SCIENCE↗