In-situ observation of single-phase compositionally-complex oxide formation during high-pressure and high-temperature synthesis
Compositionally-complex oxides (CCOs) with equal or non-equal atomic ratios of multi-principal cations are single-phase solid solutions and possess unique structural characteristics and correlated possibilities for tailorable and exceptional functionalities. However, breakdown of single-phase structure and phase separation impair widespread adoption of CCOs under in-service environments. Here, in-situ phase transformation during high-pressure and high-temperature synthesis of an exemplary CCO (CeZrHf) 0.852 (YbY) 0.148 O 2-δ is for the first time clarified by using synchrotron X-ray energy dispersive diffraction. During synthesizing at ~4.5 GPa inside a large-volume press, ZrO 2 and HfO 2 gradually initiate lattice diffusion as monoclinic (022) and (220) peaks collapse and merge completely at 973 K; CeO 2 starts diffusing as the dramatic intensity change of cubic (220) peak above 1073 K, causing a metastable phase formation; single-phase solid solution ultimately forms at 1673 K. Importantly, the results revealed provide in-depth understanding of phase transformation dynamics and insights for novel design paradigm of CCOs.