Room temperature tensile ductility in polycrystalline B2 Ni-30Al-20Fe
A room-temperature tensile elongation of about 2.5 percent, where the only slip vector observed was the 100, has been determined for a double-extruded B2 Ni-30Al-20Fe alloy consisting of recrystallized equiaxed grains about 25 microns in diameter; these results suggest that 100-slip does not preclude limited ductility in polycrystalline B2 alloys in tension at low temperatures. A suppression of ordering through resort to rapid solidification, in other words, is not necessary for ductility, since the cast and as-extruded alloy presently examined is ordered.
Improving the low temperature ductility of NiAl
As part of a study aimed at developing a ductile NiAl-based alloy, ingots of Ni-Fe-Al alloys were cast and hot extruded to rods. The purpose of the iron additions was two-fold viz; to produce a change in the slip vector from 001 to 111 line and, in one alloy, to add a L1(2)-structured ductile second phase. Extruded Ni-20Al-30Fe was two-phase, containing a pro-eutectic B2 phase in a fine lamellar structure of B2+L1(2) phases. Room temperature tensile testing of both single extruded and double extruded alloys resulted in 8-percent and 22-percent plastic elongation and yield stresses of 850 and 760 MPa, respectively. Fracture in both cases occurred by ductile tearing of the eutectic and transgranular cleavage of the proeutectic phase at 1350 MPa. The ductility in double extruded condition is higher than that reported earlier in rapidly solidified wires by Inoue et al. (1984). By comparison, extruded single-phase B2-structured Ni-30Al-20Fe exhibited a fracture strength of 780 MPa, no plasticity, and a mixture of intergranular fracture and transgranular cleavage. This is contrast to earlier work by Inoue et al. where a yield stress of 400 MPa, 5 percent plastic strain, and a mixture of dimple and intergranular fracture was reported.