DOE OSTI2026

Development of in situ thickness sensor for vapor diffused Nb3Sn films

Fermilab is one of the leaders in development of vapor diffused Nb3Sn films inside niobium cavities. This material has a higher critical temperature (Tc) than niobium, enabling cavity operation at 4.2 K. This higher operational temperature significantly reduces the infrastructure required for cooling compared to 2 K systems, making superconducting radio-frequency (SRF) technology more accessible. Current deposition methods have relied on iterative testing to determine nominal film thickness, a process that can be time-consuming and imprecise. To address this, we are developing a sensor to measure the thickness of Nb3Sn thin film in situ during vapor diffusion. Our design involves the resistance measurement of a thin film of niobium. During coating, the change in resistance reflects the conversion of the film to Nb3Sn, which allows simple integration with the current furnace infrastructure. This sensor would allow real time measurement of the thickness, allowing for increased precision in future depositions.

Howard, K. [Unlisted] (ORCID:0000000325613308)↗

DOE OSTI2026

Identifying the connections between grain growth and flux expulsion in low RRR niobium SRF cavities

The SRF community has shown that high temperature annealing can improve the flux expulsion of niobium cavities during cooldown. The required temperature will vary between cavities and different batches of material, typically around 800 C and up to 1000 C. However, for niobium with a low residual resistance ratio (RRR), even 1000 C is not enough to improve its poor flux expulsion. The purpose of this study is to observe the grain growth behavior of low RRR niobium coupons subjected to high temperature annealing to identify the mechanism for improving flux expulsion. We observe that low RRR material experiences less grain growth than high RRR when annealed at the same temperature. We search for the limitations to grain growth in low RRR material and develop a diagnostic based on grain structure to determine the appropriate recipe for good flux expulsion. The results of this study have the potential to unlock a new understanding on SRF materials and enable the next generation of high Q/high gradient surface treatments.

Howard, K. [Chicago U.] (ORCID:0000000325613308)↗

DOE OSTI2026

Development of in situ thickness sensor for vapor diffused Nb3Sn films

Fermilab is one of the leaders in development of vapor diffused Nb3Sn films inside niobium cavities. This material has a higher critical temperature (Tc) than niobium, enabling cavity operation at 4.2 K. This higher operational temperature significantly reduces the infrastructure required for cooling compared to 2 K systems, making superconducting radio-frequency (SRF) technology more accessible. Current deposition methods have relied on iterative testing to determine nominal film thickness, a process that can be time-consuming and imprecise. To address this, we are developing a sensor to measure the thickness of Nb3Sn thin film in situ during vapor diffusion. Our design involves a four-point resistance measurement of a thin film of niobium, inside the coating region. During coating, the change in resistance reflects the conversion of the film from Nb to Nb3Sn, which allows simple integration with the current furnace infrastructure. This sensor would allow real time measurement of the Nb3Sn film thickness, allowing for increased precision in future depositions for cavity applications.

Howard, K. [Chicago U.] (ORCID:0000000325613308)↗

DOE OSTI2026

Understanding the connections between grain growth and flux expulsion in low RRR niobium SRF cavities

The SRF community has shown that high temperature annealing can improve the flux expulsion of niobium cavities during cooldown. The required temperature will vary between cavities and different batches of material, typically around 800 C and up to 1000 C. However, for niobium with a low residual resistance ratio (RRR), even 1000 C is not enough to improve its poor flux expulsion. The purpose of this study is to observe the grain growth behavior of low RRR niobium coupons subjected to high temperature annealing to identify the mechanism for improving flux expulsion in low RRR cavities. We anneal the low RRR material up to 1200 C to understand the limits of flux expulsion performance. We observe that low RRR material experiences less grain growth than high RRR when annealed at the same temperature. We search for the limitations to grain growth in low RRR material and develop a diagnostic based on grain structure to determine the appropriate recipe for good flux expulsion. The results of this study have the potential to unlock a new understanding on SRF materials and enable the next generation of high Q/high gradient surface treatments.

Howard, K. [Chicago U.]↗

DOE OSTI2025

Ultracoherent SRF Cavity-Based Multi-Qudit Platform with Error-Resilient Control

Superconducting radio-frequency (SRF) cavities offer a promising platform for quantum computing due to their long coherence times, yet integrating nonlinear elements like transmons for control often introduces additional loss. We report a multimode quantum system based on a 2-cell elliptical shaped SRF cavity, comprising two cavity modes weakly coupled to an ancillary transmon circuit, designed to preserve coherence while enabling efficient control of the cavity modes. We mitigate the detrimental effects of the transmon decoherence through careful design optimization that reduces transmon-cavity couplings and participation in the dielectric substrate and lossy interfaces, to achieve single-photon lifetimes of 20.6\,ms and 15.6\,ms for the two modes, and a pure dephasing time exceeding 40\,ms. This marks an order-of-magnitude improvement over prior 3D multimode memories. Leveraging sideband interactions and novel error-resilient protocols, including measurement-based correction and post-selection, we achieve high-fidelity control over quantum states. This enables the preparation of Fock states up to $N = 20$ with fidelities exceeding 95\%, the highest reported to date to the authors' knowledge, as well as two-mode entanglement with an estimated coherence-limited fidelities of 99.9\% after post-selection. These results establish our platform as a robust foundation for quantum information processing, allowing for future extensions to high-dimensional qudit encodings.

Kim, T. [Northwestern U.]↗

DOE OSTI2025

Studies as a function of different ALD capping layers on cavity losses for QIS and accelerators

Niobium-based bulk SRF cavities have demonstrated exceptional performance. To further improve niobium cavity performance, we present studies involving a novel surface engineering process designed to prevent the formation of amorphous niobium oxides on the surface. This is achieved by encapsulating the niobium surface using thermal Atomic-Layer-Deposition (ALD). This technique has been shown to enhance the properties of niobium cavities and 2D resonators. This study not only aims to improve SRF performance at high fields but also has the potential to enhance the quality factor in low-field regimes, particularly for quantum applications. For the method to be effective, it is essential to have a clean interface between the encapsulating layer and the bulk niobium. Achieving this requires a uniform coating across the entire cavity surface and efficient removal of the underlying niobium oxides. To optimize the process, a variety of material characterization tools have been utilized to refine parameters such as thin film thickness and annealing conditions. Cavity RF measurements were performed at the vertical test facilities at FNAL to assess the Q vs. Eacc curves for accelerator applications, as well as at the SQMS dilution refrigerators to investigate the full two-level system (TLS) losses at milliKelvin and single-photon levels. Based on the results, we characterized the loss of different oxides in various regimes and applications, comparing them to natural niobium pentoxide.

Grassellino, L. [Fermilab]↗

DOE OSTI2025

Identifying the connections between grain growth and flux expulsion in low RRR niobium SRF cavities

Howard, K. [Chicago U.] (ORCID:0000000325613308)↗

DOE OSTI2025

Challenges of Vapor Diffusion $Nb_3Sn$ Coating at Fermilab: Minimizing Impurities Using TOF-SIMS

Nb$_3$Sn demonstrates steady advancements nowadays offering reduced power cost in superconducting radio-frequency cavities due to its high critical temperature, quality factor, and achieved accelerating gradient. However, theoretical estimates of its radio-frequency parameters have not been achieved due to several potentially limiting mechanisms: tin spots, patchy regions, defects, thermal impedance, and impurities. While some of these limitations have been intensively studied, impurity analysis in Nb$_3$Sn coatings have received less attention. We report an investigation of impurities in several vapor-diffused Nb$_3$Snn coated samples using time-of-flight secondary ion mass spectroscopy (TOF-SIMS) and show allowable impurity levels in view of superconducting cavity performance. Challenges and lessons learned in maintaining clean Nb$_3$Sn coatings are also discussed.

Tagdulang, N. [Fermilab]↗