Engineering topics
Publications and source records attributed to Athanasiou, Christos E..
A high temperature multibeam-optical-stress sensor (HTMOSS) was used to characterize the coefficient of thermal expansion (CTE) and yield stress of 1-micron thick Lipon films.
Metal-dendrite penetration is a mode of electrolyte failure that threatens the viability of metal-anode-based solid-state batteries. Whether dendrites are driven by mechanical failure or electrochemical degradation of solid electrolytes remains an open question. If internal mechanical forces drive failure, superimposing a compressive load that counters internal stress may mitigate dendrite penetration. Here, we investigate this hypothesis by dynamically applying mechanical loads to growing dendrites in Li 6.6 La 3 Zr 1.6 Ta 0.4 O 12 solid electrolytes. Operando microscopy reveals marked deflection in the dendrite growth trajectory at the onset of compressive loading. For sufficient loading, this deflection averts cell failure. Using fracture mechanics, we quantify the impact of stack pressure and in-plane stresses on dendrite trajectory, chart the residual stresses required to prevent short-circuit failure, and propose design approaches to achieve such stresses. For the materials studied here, we show that dendrite propagation is dictated by electrolyte fracture, with electronic leakage playing a negligible role.
Measuring fracture toughness of materials at small scales remains challenging due to limited experimental testing configurations. A recently developed indentation pillar-splitting method has shown promise of improved flexibility in fracture toughness measurements at the microscale, partly due to the occurrence of an unusual fracture instability, i.e., a transition from stable to unstable crack propagation. In spite of growing interest in this method, the underlying mechanism of this phenomenon is yet to be elucidated. Furthermore, we provide a comprehensive description of fracture instability in indentation pillar-splitting by combining in situ experiments with high-fidelity simulations based on cohesive zone and J-integral methods. In addition, a machine-learning-based solution for predicting the critical indentation load of fracture instability is established through Gaussian processes regression for broad use of this method by the community.
Wide ranging mechanical properties — elasticity, plasticity, fracture, and creep — most relevant to the mechanical reliability of perovskite solar cells (PSCs) are systematically investigated. High quality bulk single-crystals of the commonly studied metal-halide perovskites (MHPs) relevant to PSCs are fabricated and studied: CH 3 NH 3 PbBr 3 (MAPbBr 3 ) and CH 3 NH 3 PbI 3 (MAPbI 3 ). The first direct measurement of MHP Young's modulus (E) using uniaxial compression reveals E <100> of 13.1 ± 1.3 and 10.6 ± 1.0 GPa for MAPbBr 3 and MAPbI 3 , respectively. Further, the Vickers micro-hardness H (100) of MAPbBr 3 and MAPbI 3 is 0.54±0.02 GPa and 0.76±0.05 GPa, respectively. The Vickers micro-indentation fracture toughness K IC of MAPbBr 3 and MAPbI 3 is estimated at 0.20±0.03 MPa∙m 0.5 and 0.18±0.03 MPa∙m 0.5 , respectively. The stress-exponent, n, extracted from nanoindentation creep data is ~8 and ~10 for MAPbBr 3 and MAPbI 3 , respectively. The trends in these properties are discussed. These properties are best estimates and are recommended for use in future mechanical behavior and reliability analyses of MHPs and PSCs.
Two key interfaces in flexible perovskite solar cells (f-PSCs) are mechanically reinforced simultaneously: one between the electron-transport layer (ETL) and the 3D metal-halide perovskite (MHP) thin film using self-assembled monolayer (SAM), and the other between the 3D-MHP thin film and the hole-transport layer (HTL) using an in situ grown low-dimensional (LD) MHP capping layer. The interfacial mechanical properties are measured and modeled. This rational interface engineering results in the enhancement of not only the mechanical properties of both interfaces but also their optoelectronic properties holistically. As a result, the new class of dual-interface-reinforced f-PSCs has an unprecedented combination of the following three important performance parameters: high power-conversion efficiency (PCE) of 21.03% (with reduced hysteresis), improved operational stability of 1000 h T90 (duration at 90% initial PCE retained), and enhanced mechanical reliability of 10 000 cycles n88 (number of bending cycles at 88% initial PCE retained). Furthermore, the scientific underpinnings of these synergistic enhancements are elucidated.