Arca, Elisabetta

Publications and source records attributed to Arca, Elisabetta.

7 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2022

Understanding the Origin of the Nonpassivating Behavior of Si-Based Anodes during the Initial Cycles

In this contribution, we combined electrochemical cycling and X-ray photoelectron spectroscopy (XPS) to understand the nonpassivating behavior of the solid electrolyte interphase (SEI) on Si anodes during the first cycles. Based on galvanostatic measurements, we show that the irreversible capacity loss is reduced after the first cycle, and it stays almost constant from the second cycle onwards. XPS was used to determine the root causes of the Coulombic inefficiency, showing that the rate of decomposition of the organic solvents strongly decreased after the first cycle, whereas the rate of salt decomposition is almost unchanged between cycles. We determine that the inhibition of the decomposition reaction of the organic solvent is responsible for the lower Coulombic loss during the second electrochemical cycle in comparison to the first, whereas the nonpassivating behavior toward the salt decomposition is one of the main causes of capacity loss upon cycling. Here, we further revisit the role of cracking in contributing to capacity loss. Whereas high volumetric expansion remains an issue plaguing the performance of Si anodes, our chronoamperometry studies reveal that the SEI formed on Si anodes does not passivate even when the electrode is fully expanded, and no additional surface is exposed. Overall, our work establishes the need to address the chemical and electrochemical instability of the SEI on the Si anode in addition to the more notorious issue of cracking.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Heterostructured Lepidocrocite Titanate-Carbon Nanosheets for Electrochemical Applications

Lepidocrocite-type titanates that reversibly intercalate sodium ions at low potentials (~0.6 V vs Na/Na + ) are promising anode candidates for sodium-ion batteries. However, large amounts of carbon additives are often used to improve their electrical conductivity and overcome poor cycling performance in the electrode composites. To ameliorate electronic transport issues of lepidocrocite titanate (K 0.8 Ti 1.73 Li 0.27 O 4 , KTL) in sodium-ion batteries, we have designed and synthesized heterostructures of exfoliated lepidocrocite-type titanium oxide (LTO) nanosheets with alternating carbon layers via a solution-based self-assembly approach. Positively charged dopamine (Dopa) was used as the carbon precursor and intercalated between negatively charged exfoliated titania nanosheets through electrostatic interaction. Dopa-intercalated LTO was then annealed under argon to form conductive carbon layers between titania sheets. The carbon content in the heterostructures was controlled by modifying the self-assembly conditions (i.e., pH, stirring duration, and Dopa-to-LTO ratio). Electrodes were prepared using carbonized heterostructures (LTO-C) without adding more carbon to the composites and tested in sodium half-cell configurations. Further, higher capacities and improved capacity retention over 250 cycles and lower impedance were observed, as the carbon content of LTO-C heterostructures was increased from 0% (LTO nanosheets) to 30%. These results indicate that the self-assembly approach for 2D heterostructured electrode materials is a promising strategy to overcome electronic transport limitations of layered transition-metal oxides and improve their electrochemical performance for next-generation energy storage applications.

25 ENERGY STORAGE↗
DOE OSTI2020

High Current Cycling in a Superconcentrated Ionic Liquid Electrolyte to Promote Uniform Li Morphology and a Uniform LiF-Rich Solid Electrolyte Interphase

High-energy-density systems with fast charging rates and suppressed dendrite growth are critical for the implementation of efficient and safe next-generation advanced battery technologies such as those based on Li metal. However, there are few studies that investigate reliable cycling of Li metal electrodes under high-rate conditions. in this work, by employing a superconcentrated ionic liquid (IL) electrolyte, we highlight the effect of Li salt concentration and applied current density on the resulting Li deposit morphology and solid electrolyte interphase (SEI) characteristics, demonstrating exceptional deposition/dissolution rates and efficiency in these systems. Operation at higher current densities enhanced the cycling efficiency, e.g., from 64 ± 3% at 1 mA cm –2 up to 96 ± 1% at 20 mA cm –2 (overpotential <±0.2 V), while resulting in lower electrode resistance and dendrite-free Li morphology. A maximum current density of 50 mA cm –2 resulted in 88 ± 3% cycling efficiency, displaying tolerance for high overpotentials at the Ni working electrode (0.5 V). X-ray photoelectron microscopy (XPS), time-of-flight secondary-ion mass spectroscopy (ToF-SIMS), and scanning electron microscopy (SEM) surface measurements revealed that the formation of a stable SEI, rich in LiF and deficient in organic carbon species, coupled with nondendritic and compact Li morphologies enabled enhanced cycling efficiency at higher currents. Reduced dendrite formation at high current is further highlighted by the use of a highly porous separator in coin cell cycling (1 mAh cm –2 at 50 °C), sustaining 500 cycles at 10 mA cm –2 .

25 ENERGY STORAGE↗
DOE OSTI2020

Enhanced Interfacial Stability of Si Anodes for Li-Ion Batteries via Surface SiO2 Coating

Silicon is a promising alloying anode for lithium-ion batteries owing to its high capacity and low cost. However, its use has been hampered by mechanical failure arising from the large volume change upon cycling and by an insufficiently stable solid-electrolyte interphase (SEI). SEI formation depends on the Si surface, which is often an oxide (SiO x ). In this study we compare three different Si surfaces using Si wafers: 1.3 nm native SiO x , 1.4 nm thermally grown SiO2, and a SiOx-free surface. The oxide-free surface showed the worst electrochemical performance, never exceeding 94% Coulombic efficiency (CE). Furthermore, it also exhibited the thickest SEI and the highest overpotential for lithiation, which correlated with uninhibited electrolyte reduction and the incorporation of P-F species into the SEI. The oxide-coated surfaces performed significantly better, demonstrating a CE above 99% beyond the second cycle, low overpotential for lithiation, and a thinner and more stable SEI. The oxides lower the onset potential for electrolyte reduction, and yield an SEI with fewer P-F species. However, it was found that the CE with the native oxide surface decays from the fifth cycle onwards and correlates with a resurgence of electrolyte reduction. A 1-2 nm thermal SiO 2 coating is optimum for achieving a stable SEI that minimizes side reactions and sustains efficient cycling.

25 ENERGY STORAGE↗
DOE OSTI2020

Nonpassivated Silicon Anode Surface

A stable solid electrolyte interphase (SEI) has been proven to be a key enabler to most advanced battery chemistries, where the reactivity between the electrolyte and the anode operating beyond the electrolyte stability limits must be kinetically suppressed by such SEIs. The graphite anode used in state-of-the-art Li-ion batteries presents the most representative SEI example. Because of similar operation potentials between graphite and silicon (Si), a similar passivation mechanism has been thought to apply on the Si anode when using the same carbonate-based electrolytes. Herein, we found that the chemical formation process of a proto-SEI on Si is closely entangled with incessant SEI decomposition, detachment, and reparation, which lead to continuous lithium consumption. Using a special galvanostatic protocol designed to observe the SEI formation prior to Si lithiation, we were able to deconvolute the electrochemical formation of such dynamic SEI from the morphology and mechanical complexities of Si and showed that a pristine Si anode could not be fully passivated in carbonate-based electrolytes.

25 ENERGY STORAGE↗
DOE OSTI2020

Surface SiO 2 Thickness Controls Uniform-to-Localized Transition in Lithiation of Silicon Anodes for Lithium-Ion Batteries

Silicon is a promising anode material for lithium-ion batteries because of its high capacity, but its widespread adoption has been hampered by a low cycle life arising from mechanical failure and the absence of a stable solid–electrolyte interphase (SEI). Understanding SEI formation and its impact on cycle life is made more complex by the oxidation of silicon materials in air or during synthesis, which leads to SiO x coatings of varying thicknesses that form the true surface of the electrode. Here, the lithiation of SiO 2 -coated Si is studied in a controlled manner using SiO 2 coatings of different thicknesses grown on Si wafers via thermal oxidation. SiO 2 thickness has a profound effect on lithiation: below 2 nm, SEI formation followed by uniform lithiation occurs at positive voltages versus Li/Li + . Si lithiation is reversible, and SiO 2 lithiation is largely irreversible. Above 2 nm SiO 2 , voltammetric currents decrease exponentially with SiO 2 thickness. For 2–3 nm SiO 2 , SEI formation above 0.1 V is suppressed, but a hold at low or negative voltages can initiate charge transfer whereupon SEI formation and uniform lithiation occur. Cycling of Si anodes with an SiO 2 coating thinner than 3 nm occurs at high Coulombic efficiency (CE). If an SiO 2 coating is thicker than 3–4 nm, the behavior is totally different: lithiation at positive voltages is strongly inhibited, and lithiation occurs at poor CE and is highly localized at pinholes which grow over time. As they grow, lithiation becomes more facile and the CE increases. Pinhole growth is proposed to occur via rapid transport of Li along the SiO 2 /Si interface radially outward from an existing pinhole, followed by the lithiation of SiO 2 from the interface outward.

25 ENERGY STORAGE↗