Two–Photon Printing of Base–Catalyzed Resins Involving Thiol–Michael Network Formation

Two-photon printing is accomplished using a photobase generator, 2-(2-nitrophenyl)-propyloxycarbony tetramethyl guanidine, to locally catalyze thiol-ene coupling between multifunctional monomers while mitigating chain-growth polymerization with free radical scavengers. Microstructures printed from base-catalyzed resins exhibit higher resolution (linewidths < 400 nm) and lower print error (<3%) than analogous microstructures printed using a photosensitive, free radical initiator. Further, Raman spectroscopy reveals that resins polymerized using the photobase generator in the presence of free radical scavengers exhibit higher selectivity of thiol-ene coupling over radical polymerization, resulting in stiffer, more uniform polymer networks. The base-catalyzed resins are capable of producing 3D microstructures printed with high accuracy and minimal post-processing defects. As a result, a direct comparison between free radical and base-initiated resins highlights the need for mindful consideration of how chemical reaction pathway influences printability and network end-properties when designing resins.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Spatiotemporal Reaction Dynamics Control in Two‐Photon Polymerization for Enhancing Writing Characteristics

Since 2001, 3D microfabrication based on two‐photon polymerization (TPP) has drawn extensive attention and interest in biology, optics, photonics, material science, and high‐energy physics. The in‐volume fabrication capability due to the threshold behavior of two‐photon absorption enables TPP higher flexibility compared with other nanofabrication techniques. However, as determined by the in‐volume fabrication feature as well as various reaction dynamics, the writing characteristics of TPP, such as throughput, accuracy, surface quality, and fabrication capability, are still limited. Herein, a comprehensive study is performed on the spatiotemporal behavior of reaction dynamics during TPP fabrication, mainly focusing on spatiotemporal characteristics of radical diffusion, photothermal effect, microscale mechanics, and voxel stacking process. Based on the study, a nonsequential fabrication method is established to simultaneously improve key writing characteristics of TPP and realize sharp features, high speeds, large overhang structure, and smooth surfaces. The method established in this work can be applied to improve the performance of functional devices for various fields.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Two–Photon Printing of Shape–Memory Microstructures and Metasurfaces via Radical–Mediated Thiol–Vinyl Hydrothiolation

Shape-memory resists capable of high-resolution curing into arbitrarily designed structures are increasingly demanded for soft robotics, optical sensors, microscale manufacturing, and biomedicine. Amorphous, shape-memory thiol-vinyl networks were printed using two-photon polymerization (2PP) curing of a simple resin formulated with commercially available reagents. The ability to print high-resolution feature sizes down to 200 nm is attributed to the use of radicalmediated, thiol-vinyl step-growth polymerization that quickly crosslinks the resin, limiting diffusive transport. The thermomechanical behavior of the 2PP-cured material analyzed in compression, tension and three-point bending is similar to the behavior of the UV-polymerized samples. To demonstrate the ability to design, field, and test 4D responsive microstructures, an array of nine springs with coil diameters of 330 μm was printed. Following compressive shapefixing, printed arrays can release 11 μJ of stored elastic strain energy when reheated. Further, a new concept of dichroic-memory of a metamaterial device is demonstrated by printing a twisted woodpile structure with circular dichroism as characterized by Mueller Matrix ellipsometry. Furthermore, our results demonstrate how combining high-resolution 2PP curing with stimuli-responsive molecular architectures can further the engineering of responsive microstructures and metamaterials.

36 MATERIALS SCIENCE↗