Microstructure, Hardness, and Residual Stress of the Dissimilar Metal Weldments of SA508-309L/308L-304L

A dissimilar metal weldment consisting of SA508-309L-308L-304L is widely used in light-water nuclear reactors. These weldments demonstrate dissimilar susceptibility to stress corrosion cracking that are related to the microstructure, properties, and residual stress. In this work, microstructures, hardness, and the residual stress distribution of the dissimilar metal weldments were investigated, with the correlation of increased hardness in the heat-affected zone (HAZ) to the microstructure. 304L HAZ demonstrated similar grain morphology as the base material, and the increase in hardness was primarily attributed to the increased dislocation density. SA508 HAZ demonstrated a change of grain morphology resulting from the different peak temperatures and cooling rates. The increased hardness in the SA508 HAZ was attributed to the refined grain morphology, higher dislocation density, and higher number density of precipitates. A ~ 20–30-μm-wide martensitic zone formed at the fusion boundary of SA508-309L, where Cr-rich carbide precipitates were observed, with the average size and the number density of 44.1 ± 16.9 nm and 1.5 × 10 21 m ₋3 , respectively. In conclusion, residual stress results demonstrated the largest tensile stress at 309L butter, indicating its high cracking susceptibility.

36 MATERIALS SCIENCE↗
DOE OSTI2021

In situ monitoring of dislocation, twinning, and detwinning modes in an extruded magnesium alloy under cyclic loading conditions

This work investigates the microscopic deformation mechanisms of an extruded, precipitation-strengthened AZ80 magnesium (Mg) alloy subjected to strain-controlled low-cycle fatigue using in situ neutron diffraction measurements. Results demonstrate that the plastic deformation during cyclic loading is dominated by the alternating {10.2} extension twinning and detwinning mechanisms. The observed deformation mode is strongly texture and precipitate dependent. For the initial texture, the tested material has two major texture components which result in the occurrence of extension twinning during both compression and reverse tension in the first two cycles. The prolonged detwinning process in the following cycles is proposed to relieve the shear stress field of {00.2} grains, leading to the disappearance of twinning. The precipitation strengthening results in an increase of the critical resolved shear stress (CRSS) by similar to 33 MPa for the extension twinning in this AZ80 alloy. Here, the synergistic effects of the initial texture, precipitation strengthening, and load sharing of various grain families and phases contribute to the complicated evolution of dominant deformation mechanisms, among which elevated dislocation activities are believed to be responsible for the relatively poor low-cycle-fatigue lifetime when compared to other Mg alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Operando measurement of lattice strain in internal combustion engine components by neutron diffraction

Significance Internal combustion engine components experience extreme thermomechanical cycling during operation, and the continuing need to improve engine efficiency while maintaining or improving reliability drives the development of lightweight materials with improved thermal and mechanical integrity. Understanding the behavior of new materials in dynamic operation requires operando characterization tools, but conventional in situ measurements of material behavior during real engine operation are very limited, and no practical means exist to replicate such extreme dynamics for ex situ study. In this work, we demonstrate that the penetrating power of neutrons can provide noninvasive measurement of lattice strains inside components of a firing engine, enabling the operando study of complex load states and thermal gradients throughout the solid materials.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2020

Mapping of Texture and Phase Fractions in Heterogeneous Stress States during Multiaxial Loading of Biomedical Superelastic NiTi

Thermoelastic deformation mechanisms in polycrystalline biomedical-grade superelastic NiTi are spatially mapped using in situ neutron diffraction during multiaxial loading and heating. The trigonal R-phase is formed from the cubic phase during cooling to room temperature and subsequently deforms in compression, tension, and torsion. The resulting R-phase variant microstructure from the variant reorientation and detwinning processes are equivalent for the corresponding strain in tension and compression, and the variant microstructure is reversible by isothermal loading. The R-phase variant microstructure is consistent between uniaxial and torsional loading when the principal stress directions of the stress state are considered (for the crystallographic directions observed here). The variant microstructure evolution is tracked and the similarity in general behavior between uniaxial and torsional loading, in spite of the implicit heterogeneous stress state associated with torsional loading, pointed to the ability of the reversible thermoelastic transformation in NiTi to accommodate stress and strain mismatch with deformation. This ability of the R-phase, despite its limited variants, to accommodate stress and strain and satisfy strain incompatibility in addition to the existing internal stresses has significance for reducing irrecoverable deformation mechanisms during loading and cycling through the phase transformation.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Correlating work hardening with co-activation of stacking fault strengthening and transformation in a high entropy alloy using in-situ neutron diffraction

Transformation induced plasticity (TRIP) leads to enhancements in ductility in low stacking fault energy (SFE) alloys, however to achieve an unconventional increase in strength simultaneously, there must be barriers to dislocation motion. While stacking faults (SFs) contribute to strengthening by impeding dislocation motion, the contribution of SF strengthening to work hardening during deformation is not well understood; as compared to dislocation slip, twinning induced plasticity (TWIP) and TRIP. Thus, we used in-situ neutron diffraction to correlate SF strengthening to work hardening behavior in a low SFE Fe 40 Mn 20 Cr 15 Co 20 Si 5 (at%) high entropy alloy, SFE ~ 6.31 mJ m –2 . Cooperative activation of multiple mechanisms was indicated by increases in SF strengthening and γ-f.c.c. → ε-h.c.p. transformation leading to a simultaneous increase in strength and ductility. The present study demonstrates the application of in-situ, neutron or X-ray, diffraction techniques to correlating SF strengthening to work hardening.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Lattice-Distortion-Enhanced Yield Strength in a Refractory High-Entropy Alloy

Severe distortion is one of the four core effects in single-phase high-entropy alloys (HEAs) and contributes significantly to the yield strength. However, the connection between the atomic-scale lattice distortion and macro-scale mechanical properties through experimental verification has yet to be fully achieved, owing to two critical challenges: 1) the difficulty in the development of homogeneous single-phase solid-solution HEAs and 2) the ambiguity in describing the lattice distortion and related measurements and calculations. Here, a single-phase body-centered-cubic (BCC) refractory HEA, NbTaTiVZr, using thermodynamic modeling coupled with experimental verifications, is developed. Compared to the previously developed single-phase NbTaTiV HEA, the NbTaTiVZr HEA shows a higher yield strength and comparable plasticity. The increase in yield strength is systematically and quantitatively studied in terms of lattice distortion using a theoretical model, first-principles calculations, synchrotron X-ray/neutron diffraction, atom-probe tomography, and scanning transmission electron microscopy techniques. These results demonstrate that severe lattice distortion is a core factor for developing high strengths in refractory HEAs.

36 MATERIALS SCIENCE↗
DOE OSTI2020

A disordered rock salt anode for fast-charging lithium-ion batteries

Rechargeable lithium-ion batteries with high energy density that can be safely charged and discharged at high rates are desirable for electrified transportation and other applications. However, the sub-optimal intercalation potentials of current anodes result in a trade-off between energy density, power and safety. In this paper we report that disordered rock salt Li 3+ x V 2 O 5 can be used as a fast-charging anode that can reversibly cycle two lithium ions at an average voltage of about 0.6 volts versus a Li/Li + reference electrode. The increased potential compared to graphite reduces the likelihood of lithium metal plating if proper charging controls are used, alleviating a major safety concern (short-circuiting related to Li dendrite growth). In addition, a lithium-ion battery with a disordered rock salt Li 3 V 2 O 5 anode yields a cell voltage much higher than does a battery using a commercial fast-charging lithium titanate anode or other intercalation anode candidates (Li 3 VO 4 and LiV 0.5 Ti 0.5 S 2 ). Further, disordered rock salt Li 3 V 2 O 5 can perform over 1,000 charge–discharge cycles with negligible capacity decay and exhibits exceptional rate capability, delivering over 40 per cent of its capacity in 20 seconds. We attribute the low voltage and high rate capability of disordered rock salt Li 3 V 2 O 5 to a redistributive lithium intercalation mechanism with low energy barriers revealed via ab initio calculations. This low-potential, high-rate intercalation reaction can be used to identify other metal oxide anodes for fast-charging, long-life lithium-ion batteries.

25 ENERGY STORAGE↗
DOE OSTI2020

Synthesis and catalytic performance of polydopamine supported metal nanoparticles

Polydopamine (PDA) is an emerging nature-inspired biopolymer material that possesses many interesting properties including self-assembly and universal adhesion. PDA is also able to form coordination bonds with various metal ions, which can be reduced to metal nanoparticles (NPs) as a result of thermal annealing under protective environment. In this study, PDA has been utilized as a support material to synthesize Pt NPs in an aqueous solution at room temperature. The catalytic performance of the resulting PDA-Pt nanocomposite was evaluated using an electrochemical workstation which showed comparable activity to Pt/C material for hydrogen evolution reaction (HER). Furthermore, Cu, Ni, and Cu–Ni NPs supported on PDA were also obtained using this strategy with assistance of subsequent thermal annealing. The phase evolution of the NPs was studied by in-situ X-ray diffraction while the morphology of the nanoparticles was investigated using electron microscopic techniques. Preliminary results showed the NPs supported on PDA also possessed HER activity. This work demonstrates that PDA can be utilized as a potential support for synthesis of metal NPs that can be exploited in engineering applications such as catalysts.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Size effect in stainless steel thin wires under tension

Miniaturization of modern devices drives the exploration into how materials behave in small dimensions. However, the mechanical behaviors of micro-scale specimens under varied loading conditions are still challenging to characterize and predict. In this work, specimen size-dependent weakening effect was experimentally revealed in 316L stainless steel thin wires under tension with wire diameter decreasing from 200 μm down to 61 μm. The underlying mechanisms were primarily associated with surface grain softening and strain localization, which were largely dependent on the number of grains across wire diameter. Through an analog composite model with surface and interior grains that follows the Hall-Petch relation, the extent of surface grain softening was found to coincide with the flow stress reduction due to lack of boundary strengthening. Further using elasto-plastic self-consistent polycrystal modeling, the stress-strain behaviors of interior and surface grains were well described in analogy to those of bulk materials with similar-size grains and extremely large grains, respectively. Subsequently, the analog composite model well simulated the specimen size-dependent weakening effect under tension. This article provided more insights into the size effect exploration and proposed a practical model for describing size-dependent mechanical behaviors of small-scale materials to be applied to miniaturized devices.

316L stainless steel↗
DOE OSTI2020

Determination of Stress-Free Lattice Spacing (D₀) for Residual Stress Relaxation Measurement in Ni-based Superalloys by Neutron Diffraction

The residual stress and its relaxation in critical engineering components are key to structural materials reliability. The determination of residual stress in bulk engineering structures like Ni-based superalloys can be conducted by measuring the lattice strain with penetrating neutron diffraction. The state-of-the-art engineering diffraction beamline VULCAN at the Oak Ridge National Laboratory (ORNL) Spallation Neutron Source (SNS) provides the critical capability to evaluate the residual strain/stress relaxation in engineering component thanks to the high flux and event data features. By the means of residual stress/strain calculation, it is critical to accurately determine the stress-free lattice spacing d₀, which can be altered by the change of chemistry, unrelieved stress, and measurement scheme. Here we reported d₀ determination for determining residual stress relaxation and distribution in Alloy 718 superalloys after different quenching treatments. Selection of locations for d₀ measurement was discussed by considering the neutron path, attenuation and sample alignment. A dynamic d₀ that resulted from atom diffusion and chemistry change was estimated as function of time for the in-situ relaxation characterization. It demonstrated how the dynamic d₀ values may influence on the strain calculation in different thermally treated samples. The results highlight the importance of dynamic d₀ for in-situ relaxation involving chemical changes and provide guidance to the dynamic d₀ measurement and simulation.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Crystallographic orientation and spatially resolved damage in a dispersion-hardened Al alloy

The in-situ neutron diffraction technique, in combination with both the full-field crystal elasto-viscoplastic finite element model and microstructural characterization, was used to study the deformation-induced damage anisotropy in a commercial Al alloy, subjected to uniaxial tensile and cyclic loading. The simulations capture well the crystallographic-orientation-dependent lattice strain behavior. The hard grains, e.g. those orientated with the <111> and <422> orientations parallel with the uniaxial loading direction (LD), feature large Taylor factors and seem more prone to form damage-related band structures. Their effective elastic moduli decrease with the accumulation of damage, which are different from the soft grains orientated with the <200> orientation along the LD. Correlation between the distribution of voids and that of the residual lattice strain developed after failure may exist. The maximum tensile type residual lattice strain observed after failure may be resulted from the band structure formed in the hardest <111> grains. It was revealed that the band structure triggered by the hard particles could be one of sources of damage. In addition, while the specimen was obviously damaged, a fast stress relief was evidenced after unloading from the tension, especially at the beginning of unloading. Our present investigations provide a novel method for exploring the damage mechanisms of polycrystalline materials during plastic deformation.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Effect of nickel on the kinematic stability of retained austenite in carburized bearing steels – In-situ neutron diffraction and crystal plasticity modeling of uniaxial tension tests in AISI 8620, 4320 and 3310 steels

The presence of kinematically metastable retained austenite in the microstructure of bearing components can significantly affect the macro and micro-mechanical material response. In the present work, the influence of Ni on the stability of the retained austenite within three different grades of high carbon bearing steel using in-situ neutron diffraction is investigated. For the first time, the results show that presence of Ni increases the stability of the austenite in the elastic regime whereas the transformation rate remains unaffected. Crystal plasticity finite element (CPFE) modeling was used to study the deformation in these three steels and shows that the predominant factor causing the difference in mechanical behavior of these steels is the austenite stability. Finally, the elastic and plastic response of the matrix martensite was found to be identical among all specimens while the austenite demonstrates similar elastic behavior but remarkably different stabilities under monotonic loading.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Recognition of V3+/V4+/V5+ Multielectron Reactions in Na3V(PO4)2: A Potential High Energy Density Cathode for Sodium-Ion Batteries

Na3V(PO4)2 was reported recently as a novel cathode material with high theoretical energy density for Sodium-ion batteries (SIBs). However, whether V3+/V4+/V5+ multielectron reactions can be realized during the charging process is still an open question. In this work, Na3V(PO4)2 is synthesized by using a solid-state method. Its atomic composition and crystal structure are verified by X-ray diffraction (XRD) and neutron diffraction (ND) joint refinement. The electrochemical performance of Na3V(PO4)2 is evaluated in two different voltage windows, namely 2.5–3.8 and 2.5–4.3 V. 51V solid-state NMR (ssNMR) results disclose the presence of V5+ in Na2-xV(PO4)2 when charging Na3V(PO4)2 to 4.3 V, confirming Na3V(PO4)2 is a potential high energy density cathode through realization of V3+/V4+/V5+ multielectron reactions.

25 ENERGY STORAGE↗
DOE OSTI2019

Neutron transmission simulation of texture in polycrystalline materials

The application Sinpol, a novel tool for neutron transmission data analysis, is used to simulate the effect of deformation and recrystallization crystallographic textures in fcc materials. The texture is characterized using an orientation distribution function (ODF), which describes the distribution of crystal orientations over the three-dimensional orientation space. The Sinpol code combines the transmission contribution of each single crystal grain in the ODF to generate neutron transmission patterns through a polycrystalline aggregate. A series of texture components, commonly found in fcc materials, are considered and their neutron transmission calculated for further analysis of experimental data. The effect of grain statistics is investigated and the simulation results on more complex ODF textures are also presented. Finally, the neutron transmission simulations are successfully benchmarked on experimental data recorded on an additive manufactured Inconel 718 specimen.

36 MATERIALS SCIENCE↗