Development of sputtered techniques for thrust chambers

The 0.152 cm thick sputtered and copper deposits were electron beam welded to wrought copper. Tensile specimens were machined from the weld assemblies and tested at room temperature. Tensile strength approached the strength of wrought material. Elongations up to 25% were measured. Sputtered aluminum was used to fill 0.157 cm wide by 0.127 cm deep grooves in thrust chamber spool piece liners. The liners were closed out by sputtering copper from post and hollow cathodes.

Mullaly, J. R.↗

NASA NTRS1976

Development of sputtered techniques for thrust chambers

Procedures for closing out coolant passages in regeneratively cooled thrust chambers by triode sputtering, using post and hollow Cu-0.15 percent Zr cathodes are described. The effects of aluminum composite filler materials, substrate preparation, sputter cleaning, substrate bias current density and system geometry on closeout layer bond strength and structure are evaluated. High strength closeout layers were sputtered over aluminum fillers. The tensile strength and microstructure of continuously sputtered Cu-0.15 percent Zr deposits were determined. These continuous sputtered deposits were as thick as 0.75 cm. Tensile strengths were consistently twice as great as the strength of the material in wrought form.

Mullaly, J. R.↗