A High-Throughput Method to Define Additive Manufacturing Process Parameters: Application to Haynes 282
This paper demonstrates how an analytical and experimental method can be used to rapidly define the 45 additive manufacturing settings for a new alloy where the process parameters were previously unknown. A nickel-based superalloy, Haynes 282, was chosen for the analysis. An experimental matrix of focused processing parameters was predicted with a dimensionless number and 100 samples were printed using the Selective Laser Melting technique. High-throughput measurements validated the predicted process conditions needed to achieve desired density and hardness. The whole process was completed in 16 hours. The new technique was confirmed with analytical processing maps adopted by the metal additive manufacturing community. With the predicted set of process parameters, microstructural characterizations and tensile testing were used to confirm the predictions. The resultant as-fabricated microstructures have refined length scales of both microsegregation and secondary phase distributions. As a result, the mechanical properties were comparable within the predicted processing window and exhibited high strength and high ductility.