DOE OSTI2026

The Influence of Shielding Gas on the Wire-Arc Additive Manufacturing (WAAM) of Ni-Based Superalloy Haynes 282

Wire-arc additive manufacturing (WAAM) enables building large near-net-shaped parts using fast deposition rates and is attractive due to the potential cost and schedule savings. Haynes® 282® is a Ni-based superalloy with wide application in advanced power generation systems for its superior high temperature mechanical properties. High-quality WAAM H282 parts are achieved through careful process optimization, hence, we have focused on systematically characterizing the processing-structure-properties relationships over a wide range of wire-feed and travel speeds using a standard Ar30He shielding gas. Here the influence of adding 0.25-3% of H2 and CO2 to Ar-30He standard on our findings is examined. Multi-bead tracks were used to screen 20+ gas combinations to examine impact on wettability, porosity, oxidation, and grain structures. Improved multi-tracks are observed for gases with up to 1% H2 and 0.25% CO2. WAAM H282 builds within this range are examined to reveal differences in microstructure as evaluated with CT, SEM-EDS, and EBSD.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Process-Microstructure-Property Relationships in Low Heat Input Wire-Arc Additive Manufacturing (WAAM) of Ni-Based Superalloy Haynes 282

Conference presentation on WAAM process optimization on Ni-based superalloy Haynes® 282®. This alloy is targeted for advanced power generation systems for its superior high temperature mechanical properties. Wire-arc additive manufacturing (WAAM) offers attractive cost and materials savings with high deposition rates. Based on initial build process optimization, WAAM blocks were made, and screened for defects using high-throughput CT scanning. The microstructural evolution in arc energy range of 250-700 J/mm was characterized in the as-built and aged conditions, using electron microscopy. Results showed self-consistent microstructure across conditions, with grain size dependence on arc energy, MC and M6C carbides in as-built, and blocky grain boundary M23C6 in as-heat-treated condition. Further reductions in as-built porosity were explored through 20+ combinations of H2 and CO2 additions to shielding gas. Initial results show improved wetting behavior, and bead overlap with up to 1% H2 and up to 0.25% CO2. Combination of experimentally determined datasets provided comprehensive understanding of process-structure-property relationships in WAAM Haynes 282.

Haynes 282↗

DOE OSTI2025

Characterization of Build Parameters and Microstructure in Low Heat Input WAAM of Ni-Based Superalloy Haynes 282

Ni-based superalloy Haynes® 282® is being targeted for various applications in advanced power generation systems for its superior fabricability, weldability, and excellent high temperature creep and corrosion performance. This process optimization study aims to use a low heat-input, high deposition rate, controlled Gas Metal Arc Welding (GMAW) process, Cold Metal Transfer (CMT) by Fronius, attempting to achieve fully dense fabrication and possibly avoid the need for HIP. Twenty-one multilayer blocks (~25x100x40 mm3) were deposited to explore a large set of build parameters variations that focused on varying the travel speed from 14 to 42 inches per minute (ipm) and wire feed speed from 150 to 450 ipm. A strong correlation has been observed between arc energy – controlled primarily by travel and wire feed speed. Initial visual inspection, internal microstructural examination, and computed tomography (CT) have been used to determine the effects of built parameters on evolution of internal porosity and defects. Scanning electron microscopy techniques enabled structural and compositional imaging of heterogeneity and changes in microstructural properties.

additive manufacturing↗

DOE OSTI2025

Characterization of Build Parameters and Microstructure in Low Heat Input WAAM of Ni-Based Superalloy Haynes 282

Ni-based superalloy Haynes® 282® is being targeted for various applications in advanced power generation systems for its superior fabricability, weldability, and excellent high temperature creep and corrosion performance. This process optimization study aims to use a low heat-input, high deposition rate, controlled Gas Metal Arc Welding (GMAW) process, Cold Metal Transfer (CMT) by Fronius, attempting to achieve fully dense fabrication and possibly avoid the need for HIP. Twenty-one multilayer blocks (~25x100x40 mm3) were deposited to explore a large set of build parameters variations that focused on varying the travel speed from 14 to 42 inches per minute (ipm) and wire feed speed from 150 to 450 ipm. A strong correlation has been observed between arc energy – controlled primarily by travel and wire feed speed. Initial visual inspection, internal microstructural examination, and computed tomography (CT) have been used to determine the effects of built parameters on evolution of internal porosity and defects. Scanning electron microscopy techniques enabled structural and compositional imaging of heterogeneity and changes in microstructural properties.

additive manufacturing↗