Engineering topics

Abraham, Daniel P. (ORCID:0000000304029620)

Publications and source records attributed to Abraham, Daniel P. (ORCID:0000000304029620).

4 records

DOE OSTI2024

Unraveling Morphology and Chemistry Dynamics in Fluoroethylene Carbonate Generated Silicon Anode Solid Electrolyte Interphase Across Delithiated and Lithiated States: Relative Cycling Stability Enabled by an Elastomeric Polymer Matrix

The silicon solid electrolyte interphase (SEI) faces cyclical cracking and reconstruction due to the ∼350% volume expansion. Understanding the SEI dynamic morphology and chemistry evolution from delithiated to lithiated states is thereby paramount to engineering a stable Si anode. Fluoroethylene carbonate (FEC) is a preferred additive with widely demonstrated enhancement of the Si cycling. Thus, insights into the dynamics of the FEC-SEI may provide hints toward engineering the Si interface. Herein, complementary ATR-FTIR, AFM, tip IR, and XPS probing reveal the presence of an elastomeric polycarbonate-like matrix in the FEC-generated SEI which is absent from the FEC-free SEI. Adding FEC to the baseline 1 M LiPF 6 in EC:EMC (1:1) electrolyte promotes formation of a thinner and more conformal SEI, and subdues morphology and chemistry changes between consecutive half-cycles. From AFM, morphological stabilization of the FEC-SEI occurs earlier. Furthermore, conventional SEI biproducts such as Li 2 CO 3 and LiEDC appear in reduced quantities in the FEC-SEI implying a reduced quantity of Li-consuming species. The thin polymeric FEC-SEI enables deeper (de)lithiation of silicon. In conclusion, the enhanced mechanical compliance, chemical invariance, and reduced Li inventory consumption of the FEC-SEI are logically the key features underlying the Si cycling enhancement by FEC.

25 ENERGY STORAGE↗

DOE OSTI2022

Carbon-Binder Weight Loading Optimization for Improved Lithium-Ion Battery Rate Capability

Battery performance is strongly correlated with electrode microstructure and weight loading of the electrode components. Among them are the carbon-black and binder additives that enhance effective conductivity and provide mechanical integrity. However, these both reduce effective ionic transport in the electrolyte phase and reduce energy density. Therefore, an optimal additive loading is required to maximize performance, especially for fast charging where ionic transport is essential. Such optimization analysis is however challenging due to the nanoscale imaging limitations that prevent characterizing this additive phase and thus quantifying its impact on performance. Herein, an additive-phase generation algorithm has been developed to remedy this limitation and identify percolation threshold used to define a minimal additive loading. Improved ionic transport coefficients from reducing additive loading has been then quantified through homogenization calculation, macroscale model fitting, and experimental symmetric cell measurement, with good agreement between the methods. Rate capability test demonstrates capacity improvement at fast charge at the beginning of life, from 37% to 55%, respectively for high and low additive loading during 6C CC charging, in agreement with macroscale model, and attributed to a combination of lower cathode impedance, reduced electrode tortuosity and cathode thickness.

25 ENERGY STORAGE↗

DOE OSTI2022

Critical Evaluation of Potentiostatic Holds as Accelerated Predictors of Capacity Fade during Calendar Aging

Li-ion batteries will lose both capacity and power over time due to calendar aging caused by slow parasitic processes that consume Li + ions. Studying and mitigating these processes is traditionally an equally slow venture, which is especially taxing for the validation of new active materials and electrolyte additives. Here, we evaluate whether potentiostatic holds can be used to accelerate the diagnosis of Li + loss during calendar aging. The technique is based on the idea that, under the right conditions, the current measured as the cell voltage is held constant can be correlated with the instantaneous rate of side reactions. Thus, in principle, these measurements could capture the rate of capacity fade in real time . In practice, we show that this method is incapable of quantitatively forecasting calendar aging trends. Instead, our study demonstrates that potentiostatic holds can be applied for initial qualitative screening of systems that exhibit promising long-term stability, which can be useful to shrink the parameter space for calendar aging studies. By facilitating the identification of improved formulations, this approach can help accelerate innovation in the battery industry.

25 ENERGY STORAGE↗

DOE OSTI2022

Electrochemical Modeling and Experimental Verification of Lithiation Gradients in Oxide Cathodes of Lithium-Ion Cells

Lithiated nickel-cobalt-manganese oxides, such as NCM523, are used in the positive electrode (cathode) of Li-ion cells. Using operando X-ray diffraction profilometry, lithiation gradients in the cathode matrix can be observed and quantified by expansion into Legendre polynomials with time-dependent weights. These weights (referred to as gradients) increase in magnitude when electric current flows through the cell, decrease during potentiostatic hold and finally relax to zero when the current is interrupted during open circuit rest. Both physics-based electrochemical models and operando X-ray experiments suggest that the time constants for gradient growth and abatement are primarily determined by ionic diffusion in the oxide particles, which in turn depends on their lithium content. In contrast, the magnitude of gradients depends mainly on the applied current. The X-ray profilometry provides a way of directly probing the formation and disappearance of Li gradients across the cathode during fast cycling, which can help to diagnose the effects of material degradation in the cells.

25 ENERGY STORAGE↗